ALCUDIA® EVA PA-440
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® EVA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GlV8Ym_ALCUDIA-EVA-PA-440.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EVA resin ALCUDIA® PA-440 is recommended for hot melt adhesives applications, injection moulding and extrusion of profiles. It contains antioxidant and free flowing agent. TYPICAL APPLICATIONS
Recommended melt temperature below 200°C to avoid the decomposition of the polymer. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.950 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Vinyl Acetate Content | 28.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A | 80 | ||
| Shore D | 28 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 22.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 760 | % | ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 75.0 | °C | |
| Ring and Ball Softening Point | 142 | °C | ASTM E28 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brookfield Viscosity 1(200°C) | 1770000 | mPa·s | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 | °C |
| Note Message | |
|---|---|
| 1 . | Spindle SC4-27 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Axiall PVC 12882 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| POLYCOMPO PE 2100J | POLYCOMPO Co.,Ltd. | HDPE | POLYCOMPO PE |
| Hostacom PPU X9067HS G62514 | LyondellBasell Industries | PP Copolymer | Hostacom |
| PONACOM PS 5380 | Ponachem Compound GmbH | PS (HIPS) | PONACOM PS |
| LNP™ LUBRICOMP™ GL004 compound | SABIC Innovative Plastics | PSU | LNP™ LUBRICOMP™ |