Sindustris ABS LXR512T
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gl6MYn_Sindustris-ABS-LXR512T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris ABS LXR512T is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris ABS LXR512T are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield, 3.20 mm | > 5.0 | % | |
| Break, 3.20 mm | 15 | % | |
| Flexural Modulus 3(3.20 mm) | 27000 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 79.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 69 | J/m | |
| -30°C, 6.40 mm | 69 | J/m | |
| 23°C, 3.20 mm | 160 | J/m | |
| 23°C, 6.40 mm | 150 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 103 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 95.0 | °C | |
| Vicat Softening Temperature | 102 | °C | ASTM D1525 5 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 15 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 33 | kV/mm | ASTM D149 |
| Arc Resistance | 6.00 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) 6 | PLC 0 | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 180 to 210 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 230 to 240 | °C | |
| Nozzle Temperature | 230 to 240 | °C | |
| Processing (Melt) Temp | 220 to 240 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| 6 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teflon® PFA 450HP | DuPont Fluoropolymers | PFA | Teflon® PFA |
| ATTANE™ 4404G | The Dow Chemical Company | ULDPE | ATTANE™ |
| HiFill® TPU/I GF40 | Techmer Engineered Solutions | TPU-Polyether | HiFill® |
| Karina CLEAR PVC COMPOUND 75/200 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ MB006HS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |