Larton GCE/600
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Larton |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GkHq1h_Larton-GCE-600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyphenylene Sulphide (PPS) based compound. Glass fibres / Mineral filler. Intrinsically flame retardant. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.85 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.15 to 0.30 | % | |
| Flow : 2.00 mm | 0.10 to 0.25 | % | |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 18500 | MPa | |
| 60°C | 18000 | MPa | |
| 90°C | 17000 | MPa | |
| 120°C | 11500 | MPa | |
| 150°C | 9100 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 165 | MPa | |
| Break, 60°C | 145 | MPa | |
| Break, 90°C | 125 | MPa | |
| Break, 120°C | 100 | MPa | |
| Break, 150°C | 85.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 0.90 | % | |
| Break, 60°C | 1.0 | % | |
| Break, 90°C | 1.1 | % | |
| Break, 120°C | 1.7 | % | |
| Break, 150°C | 2.5 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 6.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 20 | kJ/m² | |
| 23°C | 20 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 280 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 270 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 220 | °C | |
| Vicat Softening Temperature | 255 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 5.0E-6 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Oxygen Index | 45 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Regrind | 15 | % | |
| Processing (Melt) Temp | 290 to 330 | °C | |
| Mold Temperature | 130 to 140 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® PC/ABS 2512-U | Plastic Solutions, Inc. | PC+ABS | PrimaFlex® |
| Multi-Flex® TPE SiE A8508 EU1 | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| Braskem PE SBF0323/12HC | Braskem America Inc. | LDPE | Braskem PE |
| Clariant Nylon 6/6 6608G33 BLACK | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Karina PVC COMPOUD WHITE COLOR - E-800-10/1-AY-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |