NAXALOY® 793A3 GF10
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | MRC Polymers, Inc. |
| Trademark: | NAXALOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GkGgA2_NAXALOY-793A3-GF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NAXALOY® 793A3 GF10 is a Polycarbonate + Polyester (PC+Polyester) material filled with 10% glass fiber. It is available in North America for injection molding. Primary attribute of NAXALOY® 793A3 GF10: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.20 mm | 0.20 to 0.50 | % | |
| Across Flow : 3.20 mm | 0.40 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C, 3.20 mm) | 69.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C, 3.20 mm) | 5.0 | % | ASTM D638 |
| Flexural Modulus (23°C, 3.20 mm) | 3100 | MPa | ASTM D790 |
| Flexural Strength (23°C, 3.20 mm) | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 132 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 110 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTAL PM3007G6 | Polyram Ram-On Industries | Acetal (POM) Copolymer | RAMTAL |
| THERMORUN® QT99ZA | Mitsubishi Chemical Corporation | TPO (POE) | THERMORUN® |
| Hybrid PC/ABS 120 BK | Ravago Manufacturing Americas, LLC | PC+ABS | Hybrid |
| Iupital® F30-03 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| EPAMOULD 660A26 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |