TRIBOCOMP® PA6 GF40 TS5
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GiywtG_TRIBOCOMP-PA6-GF40-TS5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tribosystem 5 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.56 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.30 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| 23°C | 12000 | MPa | ISO 527-2 |
| 90°C | 5000 | MPa | ISO 527-2 |
| 120°C | 4500 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture, 23°C | 190 | MPa | ISO 527-2 |
| Fracture, 90°C | 95.0 | MPa | ISO 527-2 |
| Fracture, 120°C | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 11000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 250 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 | ||
| Dynamic | 0.21 | ASTM D3702 | |
| Static | 0.19 | ASTM D3702 | |
| Wear Factor | 10.0 | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 80 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 215 | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 2.8E-5 | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.31 | W/m/K | ISO 22007 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | ASTM D257 |
| Dielectric Strength (2.00 mm) | 36 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 230 - 270 | °C | |
| Middle Temperature | 235 - 280 | °C | |
| Front Temperature | 235 - 280 | °C | |
| Nozzle Temperature | 235 - 290 | °C | |
| Processing (Melt) Temp | < 320 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2100N0W | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Ultraform® N 2650 Z6 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Badaprene® TPV 75A 1009 | Bada AG | PP+EPDM | Badaprene® |
| Jam PE 20X02 | Jam Petrochemical Company | LLDPE | Jam PE |
| Catalyst CT/7-LR UV LB | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |