LNP™ STAT-LOY™ K3000SZ compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GiNHqy_LNP-STAT-LOY-K3000SZ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY K3000SZ is a compound based on Acetal Copolymer resin. Added feature of this material is: AntiSstatic. Also known as: LNP* STAT-LOY* Compound K-E HS Product reorder name: K3000SZ |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.32 | g/cm³ | ASTM D792 |
| -- | 1.33 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 1.8 | % | |
| Across Flow : 24 hr | 1.8 | % | |
| Water Absorption (24 hr, 50% RH) | 2.2 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1600 | MPa | ASTM D638 |
| -- | 1500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 41.4 | MPa | ASTM D638 |
| Yield | 42.0 | MPa | ISO 527-2 |
| Break | 31.7 | MPa | ASTM D638 |
| Break | 36.2 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 16 | % | ASTM D638 |
| Yield | 13 | % | ISO 527-2 |
| Break | 60 | % | ASTM D638 |
| Break | 49 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1440 | MPa | ASTM D790 |
| -- | 1500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 48.3 | MPa | ASTM D790 |
| -- | 40.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.42 | ||
| vs. Itself - Static | 0.24 | ||
| Wear Factor - Washer | 14.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D256 |
| 23°C 2 | 16 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 29.0 | J | ASTM D3763 |
| -- | 17.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 146 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 67.8 | °C | |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.3E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.3E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 to 1.0E+11 | ohms | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenopom® POM B3 M2 NTLA014 PR302 MSP | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| NuSil R-2615 | NuSil Technology | Silicone | NuSil |
| ACCUGUARD™ POL050G10HIV0L | ACLO Compounders Inc. | PC | ACCUGUARD™ |
| Hifax 7334 XEP | LyondellBasell Industries | TPO (POE) | Hifax |
| Deprene 153-50 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |