Latigea B01 L/07
| Category: | PLA , Polylactic Acid |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latigea |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gi3vSD_Latigea-B01-L-07.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bio-Polymer (PLA, PHB, ...) based compound. Wood flour. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.20 to 0.60 | % | |
| Flow : 2.00 mm | 0.15 to 0.55 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3500 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 60.0 | MPa | |
| Break, 23°C | 60.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 2.3 | % | |
| Break, 23°C | 3.5 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 55.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 60.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 40.0 to 50.0 | °C | |
| Drying Time | 6.0 | hr | |
| Processing (Melt) Temp | 170 to 190 | °C | |
| Mold Temperature | 15.0 to 30.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Menzolit® SMC 1600 | Menzolit Ltd (UK) | Polyester, TS | Menzolit® |
| Novalloy-B B6508 | PlastxWorld Inc. | ABS+PBT | Novalloy-B |
| Bakelite® PF 6507 | Hexion Inc. | Phenolic | Bakelite® |
| Exac FEP | Saint Gobain - Norton | FEP | Exac |
| Moplen HP552R | LyondellBasell Industries | PP Homopolymer | Moplen |