Starex VE-1890 K
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ghk2an_StarexVE1890K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Starex VE-1890 K is a high impact polystyrene product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 13 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.20 - 0.60 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.20 - 0.60 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.20 - 0.60 | % | ISO 2577 |
| Traffic : 3.20mm | 0.20 - 0.60 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 96 | ASTM D785 | |
| R scale | 96 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 20.0 | MPa | ASTM D638 |
| Yield | 24.0 | MPa | ISO 527-2/50 |
| Fracture | 20.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 33 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 1600 | MPa | ASTM D790 |
| -- 3 | 1700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 26.0 | MPa | ASTM D790 |
| -- 5 | 37.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 98 | J/m | ASTM D256 |
| 23°C 7 | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 4.00mm | 79.0 | °C | ISO 75-2/B |
| 0.45 MPa, annealing, 4.00mm | 84.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 72.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 68.0 | °C | ISO 75-2/A |
| 1.8 MPa, annealing, 4.00mm | 79.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 82.0 | °C | ISO 306/B50 |
| -- | 85.0 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | V-1 | UL 94 | |
| 2.0 mm | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 20 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4mm |
| 7 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4605 TFE 15 | RTP Company | SPS | RTP |
| AXELERON™ CX 6944 NT CPD | The Dow Chemical Company | HDPE | AXELERON™ |
| Plaslube® POM CO TS20 | Techmer Engineered Solutions | Acetal (POM) Copolymer | Plaslube® |
| Sylvin 83045-67 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Dryflex® V 70A101 | ELASTO | TPV | Dryflex® |