| EPO-TEK® 354 is a two component, high Tg epoxy designed for semiconductor packaging in medical, fiber optic and optoelectronic assemblies. It is an electrically and thermally insulating epoxy. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Ion Type | |||
| Cl- | 81 | ppm | |
| K+ | 9 | ppm | |
| Na+ | 17 | ppm | |
| NH4+ | 300 | ppm |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Degradation Temperature | 487 | °C | TGA |
| Die Shear Strength - >10 kg (23°C) | 23.4 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 250 | °C | |
| Intermittent | -55 to 350 | °C | |
| Storage Modulus (23°C) | 2.46 | GPa | |
| Weight Loss on Heating | |||
| 200°C | 0.50 | % | |
| 250°C | 0.70 | % | |
| 300°C | 0.85 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 95.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 9.6E-5 | cm/cm/°C | |
| -- 3 | 1.8E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index 4 | 1.573 | ||
| Transmittance | |||
| 600 nm | > 96.0 | % | |
| 800 nm | > 99.0 | % |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 5 | Amber | ||
| -- 6 | Clear/Transparent | ||
| Density | |||
| Part B | 1.15 | g/cm³ | |
| Part A | 1.20 | g/cm³ | |
| Viscosity 7(23°C) | 4.0 to 6.0 | Pa·s | |
| Curing Time (150°C) | 1.0 | hr | |
| Pot Life | 4300 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 82 | ||
| Lap Shear Strength (23°C) | 11.5 | MPa | |
| Relative Permittivity (1 kHz) | 3.48 | ||
| Volume Resistivity (23°C) | > 2.0E+13 | ohms·cm | |
| Dissipation Factor (1 kHz) | 4.0E-3 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | 589 nm |
| 5 . | Part B |
| 6 . | Part A |
| 7 . | 50 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA66 ZRPA66 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 66 | Shandong PA66 |
| Aurora PVC AP2290 Series | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| LNP™ STAT-KON™ DEL329EP compound | SABIC Innovative Plastics Europe | PC | LNP™ STAT-KON™ |
| Panlite® BN-8110R | TEIJIN LIMITED | PC | Panlite® |
| Sylvin 4200-85 Brown 7443 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |