TECHNYL® ALLOY KC 226 NATURAL
| Category: | Nylon 6+ABS , Polyamide 6 + ABS |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ggxa4G_TECHNYLALLOYKC226NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® ALLOY KC 226 Natural is an unfilled grade based on blend of polyamide 6 and acrylonitrile butadiene styrene (PA6 + ABS), for injection moulding. This grade offers high mechanical properties, good dimensional stability and good processability. It is a synergistic blend material between Polyamide 6 and ABS with an ideal property combination, meaning that it has dual characteristics between semi-crystalline and amorphous polymers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.12 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 0.90 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | 1400 | MPa | ISO 527-2/1A |
| Tensile Stress (Break, 23°C) | 65.0 | 42.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break, 23°C) | 20 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2900 | 1350 | MPa | ISO 178 |
| Flexural Stress (23°C) | 100 | 55.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact (23°C) | 6.0 | 20 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | No Break | -- | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 115 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 75.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 220 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.6 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.6 mm) | 750 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 235 - 240 | °C | |
| Middle Temperature | 240 - 250 | °C | |
| Front Temperature | 250 - 260 | °C | |
| Mold Temperature | 60 - 90 | °C |
| Injection instructions |
|---|
| The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For unfilled polyamide, Solvay recommends the use of high alloy steel with a weak chromium content. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 AR 10 TFE 20 | RTP Company | Acetal (POM) Copolymer | RTP |
| SUPREME GPPS SC205 | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| WELLAMID Nylon 6000/52 GV 15 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| HFFR 2005 | Teknor Apex Company | Polyolefin, Unspecified | HFFR |
| SECCO K7926 | Shanghai SECCO Petrochemical Co., Ltd | PP Copolymer | SECCO |