Pibiflex® E5332 NATURALE
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Pibiflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GgsGGb_Pibiflex-E5332-NATURALE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extrusion TPC grade, medium flexural modulus |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 53 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 35.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 600 | % | ASTM D638 |
| Flexural Modulus | 220 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 62.0 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 1 | 120 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 800 | J/m | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 180 | °C | ASTM D1525 2 |
| Peak Melting Temperature | 200 | °C | ASTM D3417 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 20 | % | ASTM D2863 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fatigue Resistance | 0.1/300 | kCycles | ASTM D1052 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 220 | °C | |
| Middle Temperature | 240 | °C | |
| Front Temperature | 250 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| 2 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1012H | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| RAMTAL PM340S4 | Polyram Ram-On Industries | Acetal (POM) Copolymer | RAMTAL |
| Styromer e-S0799 | Inverko Compounding B.V. | PS (GPPS) | Styromer |
| Vipel® K190-BTT-00 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| BP Flex 7000 VPL BLK | Buckeye Polymers, Inc. | TPV | BP Flex |