NORYL™ EXNL0143 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GggltY_NORYL-EXNL0143-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL PX1736 Resin is a blend of PPE and PS, that provides high strength, increased heat resistance, and translucency. The material has melt strenght suitable for Extrusion and Blow Molding applications. Typical applications include High Performance Applications. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 25 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 26.1 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.25 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2780 | MPa | ASTM D638 |
| -- | 3120 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 79.6 | MPa | ASTM D638 |
| Yield | 79.1 | MPa | ISO 527-2/50 |
| Fracture 3 | 56.0 | MPa | ASTM D638 |
| Fracture | 72.4 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 29 | % | ASTM D638 |
| Yield | 4.7 | % | ISO 527-2/50 |
| Fracture 5 | 5.2 | % | ASTM D638 |
| Fracture | 7.6 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2940 | MPa | ASTM D790 |
| -- 7 | 2980 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 124 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 125 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 3.7 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 28 | J/m | ASTM D256 |
| 23°C | 35 | J/m | ASTM D256 |
| -30°C 10 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 4.1 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 9.24 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 123 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 123 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 141 | °C | ASTM D1525, ISO 306/B50 10 13 |
| -- | 143 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 8.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 2.0E-4 | % | |
| Cylinder Zone 1 Temp. | 204 - 227 | °C | |
| Cylinder Zone 2 Temp. | 216 - 238 | °C | |
| Cylinder Zone 3 Temp. | 238 - 266 | °C | |
| Cylinder Zone 4 Temp. | 238 - 266 | °C | |
| Adapter Temperature | 238 - 266 | °C | |
| Melt Temperature | 266 - 277 | °C | |
| Die Temperature | 238 - 266 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 8 hrsRoll Stack Temp - Bottom: 104 - 121 °CRoll Stack Temp - Middle: 104 - 121 °CRoll Stack Temp - Top: 104 - 121 °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TUFNYL® SGF 30 BLUE | SRF Ltd. | Nylon 6 | TUFNYL® |
| biofila® linen | twoBEars GbR | Biodeg Polymers | biofila® |
| Favorite REG100 | Favorite Plastics | PE, Unspecified | Favorite |
| Hanwha Total PP KH52T | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| ULTEM™ 2212EPR resin | SABIC Innovative Plastics | PEI | ULTEM™ |