POCAN® DP CF 2200 000000

Category:	PC+PBT , Polycarbonate + PBT
Manufacturer:	LANXESS GmbH
Trademark:	POCAN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	GgWtkx_POCANDPCF2200000000.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
PBT+PC, non-reinforced, injection molding, flame retardant, improved impact strength, low tendency to warp

General Information
Features	Impact resistance, good Flame retardancy
Agency Ratings	EC 1907/2006 (REACH)
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.31	g/cm³	ISO 1183
Apparent Density	0.80	g/cm³	ISO 60
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg)	15.0	cm³/10min	ISO 1133
Molding Shrinkage			ISO 294-4
Vertical flow direction : 250°C, 2.00mm ¹	0.90	%	ISO 294-4
Vertical flow direction : 120°C, 2 hours, 2.00mm ²	0.50	%	ISO 294-4
Flow direction : 250°C, 2.00mm ³	0.90	%	ISO 294-4
Flow direction : 120°C, 2 hours, 2.00mm ⁴	0.50	%	ISO 294-4

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	104	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	2400	MPa	ISO 527-2/1
Tensile Stress (Yield, 23°C)	45.0	MPa	ISO 527-2/50
Tensile Strain (Yield, 23°C)	2.9	%	ISO 527-2/50
Nominal Tensile Strain at Break (23°C)	> 15	%	ISO 527-2/50
Flexural Modulus ⁵(23°C)	2500	MPa	ISO 178/A
Flexural Stress ⁶
3.5% strain	70.0	MPa	ISO 178/A
23°C	75.0	MPa	ISO 178
Flexural Strain at Flexural Strength ⁷(23°C)	5.0	%

Additional Information	Nominal Value		Test Method
ISO Shortname	PBT+PC, GFHLMPR, 09-020; ISO1043-(PBT+PC) FR (17)		ISO 7792

Injection	Nominal Value	Unit	Test Method
Admissible Residence Time at Tmax		min
Residual Moisture Content	0.0 - 0.020	%	Karl Fisher

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	< 10	kJ/m²	ISO 179/1eA
23°C	10	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	170	kJ/m²	ISO 179/1eU
23°C	No Break		ISO 179/1eU
Notched Izod Impact			ISO 180/1A
-30°C	< 10	kJ/m²	ISO 180/1A
0°C	11	kJ/m²	ISO 180/1A
23°C	10	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength			ISO 180/1U
-30°C	150	kJ/m²	ISO 180/1U
23°C	No Break		ISO 180/1U

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	95.0	°C	ISO 75-2/B
1.8 MPa, not annealed	75.0	°C	ISO 75-2/A
Vicat Softening Temperature	118	°C	ISO 306/B120
Ball Pressure Test (115°C)	Pass		IEC 60695-10-2
Melting Temperature ⁸	225	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : 23 to 55°C	8.0E-5	cm/cm/°C	ISO 11359-2
Lateral : 23 to 55°C	1.0E-4	cm/cm/°C	ISO 11359-2

Electrical	Nominal Value	Unit	Test Method
Relative Permittivity			IEC 60250
23°C, 100 Hz	3.30		IEC 60250
23°C, 1 MHz	2.90		IEC 60250
Dissipation Factor			IEC 60250
23°C, 100 Hz	0.025		IEC 60250
23°C, 1 MHz	0.014		IEC 60250
Comparative Tracking Index (Solution A)	300	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (0.750 mm)	V-0		UL 94
Glow Wire Flammability Index (0.800 mm)	960	°C	IEC 60695-2-12
Glow Wire Ignition Temperature			IEC 60695-2-13
0.800 mm	800	°C	IEC 60695-2-13
1.60 mm	800	°C	IEC 60695-2-13
3.00 mm	800	°C	IEC 60695-2-13

Injection	Nominal Value	Unit	Test Method
Drying Temperature - Circulation Dryer	120	°C
Drying Time - Circulation Dryer	4.0 - 8.0	hr
Processing (Melt) Temp	240 - 260	°C
Mold Temperature	60.0 - 80.0	°C

Note Message
1 .	60x60x2; WZ 60°C; 600 Bar
2 .	60x60x2
3 .	60x60x2; WZ 60°C; 600 Bar
4 .	60x60x2
5 .	2.0 mm/min
6 .	2.0 mm/min
7 .	Pull Rate: 2 mm/min; 50% RH
8 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
RTP 4005.3	RTP Company	PPA	RTP
Tarnoform® 300 EC2	Grupa Azoty S.A.	Acetal (POM) Copolymer	Tarnoform®
UNISOFT ADHESION™ AD-55A-NT-1-01	UNITED SOFT PLASTICS, Inc.	SEBS	UNISOFT ADHESION™
Novalloy-C CB4830	Daicel Polymer Ltd.	PC+Polyester	Novalloy-C
Sylvin 8389-95 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin