TOTAL Polyethylene LDPE FE 8004

Category:	LDPE , Low Density Polyethylene
Manufacturer:	TOTAL Refining & Chemicals
Trademark:	TOTAL Polyethylene
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Gg7yeB_TOTAL-Polyethylene-LDPE-FE-8004.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
LDPE FE 8004 is a low density polyethylene produced by a high pressure autoclave process. LDPE FE 8004 is a slip and anti-block formulated grade, which is particularly suitable for transparent thin film. LDPE FE 8004 is suited to many applications in the field of consumer, industrial, food or hygiene packaging such as collation shrink, lamination and coextrusion film.

General Information
Additive	Anti-caking agent (500 ppm) Sliding agent (650 ppm)
Features	smoothness Anti-caking property
Uses	Packaging Films Laminate Bags Industrial application Food packaging Shrinkable film Consumer goods application field
Agency Ratings	EC 1907/2006 (REACH)
Forms	Particle
Processing Method	Blow film Co-extrusion molding

Physical	Nominal Value	Unit	Test Method
Density
--	0.924	g/cm³	ISO 1183
--	924	kg/m³	ISO 1183 ¹
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.80	g/10 min	ISO 1133
Melt volume-flow rate (190°C/2.16 kg)	1.00	cm³/10min	ISO 1133 ²
Water Absorption (Saturation)	0.010	%	ISO 62 ³

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	240	MPa	ISO 527-2 ⁴
Tensile Stress (Yield)	12.0	MPa	ISO 527-2 ⁵
Tensile Strain (Yield)	15	%	ISO 527-2 ⁶
Tensile Elongation at Break	> 50	%	ISO 527-2 ⁷

Films	Nominal Value	Unit	Test Method
Tensile Stress			ISO 527-3
MD : Yield, 40 µm, blown film	12.5	MPa	ISO 527-3
TD : Yield, 40 µm, blown film	12.5	MPa	ISO 527-3
MD : Broken, 40 µm, blown film	28.0	MPa	ISO 527-3
TD : Broken, 40 µm, blown film	24.0	MPa	ISO 527-3
Tensile Elongation			ISO 527-3
MD : Broken, 40 µm, blown film	370	%	ISO 527-3
TD : Broken, 40 µm, blown film	570	%	ISO 527-3
Dart Drop Impact (40 µm, Blown Film)	120	g	ISO 7765-1

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa)	41.0	°C	ISO 75-2 ⁸
Vicat Softening Temperature
--	99.0	°C	ISO 306
50°C/h, B (50N)	98.0	°C	ISO 306 ⁹
Melting Temperature (DSC)
--	111	°C	ISO 3146
-- ¹⁰	114	°C	ISO 11357-3 ¹¹
CLTE - Flow	1.8E-4	cm/cm/°C	ISO 11359-2 ¹²

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+14	ohms	IEC 60093 ¹³
Volume Resistivity	> 1.0E+13	ohms·m	IEC 60093 ¹⁴
Relative Permittivity (100 Hz)	2.00		IEC 60250 ¹⁵
Dissipation Factor			IEC 60250 ¹⁶
100 Hz	2.0E-4		IEC 60250
1 MHz	2.0E-4		IEC 60250
Comparative Tracking Index	600		IEC 60112 ¹⁷

Flammability	Nominal Value	Unit	Test Method
Burning Behav. at 1.6mm nom. thickn. (1.60 mm)	HB		ISO 1210 ¹⁸
Oxygen Index	18	%	ISO 4589-2 ¹⁹

Additional Information
The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.Elmendorf, ISO 6383-2, MD, Blown Film, 40 µm: 53 N/mmElmendorf, ISO 6383-2, TD, Blown Film, 40 µm: 47 N/mmHaze, ISO 14782, Blown Film, 40 µm: 12%

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	160 - 200	°C
Cylinder Zone 2 Temp.	160 - 200	°C
Cylinder Zone 3 Temp.	160 - 200	°C
Cylinder Zone 4 Temp.	160 - 200	°C
Cylinder Zone 5 Temp.	160 - 200	°C

Note Message
1 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
2 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
3 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
4 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
5 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
6 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
7 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
8 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
9 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
10 .	10 °C/min
11 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
12 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
13 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
14 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
15 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
16 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
17 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
18 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
19 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???

Resin Grade	Manufacturer	Category	Trademark
Sinvicomp SRG6465	Teknor Apex Asia Pacific PTE. LTD.	PVC, Flexible	Sinvicomp
Bergamid™ B700 G15 H	PolyOne Corporation	Nylon 6	Bergamid™
OmniCarb™ PC/PBT 1214 IM	OMNI Plastics, LLC	PC+PBT	OmniCarb™
POLYfill PPH T10020	Polykemi AB	PP Homopolymer	POLYfill
Lucon® PS6050	LG Chem Ltd.	ABS	Lucon®