Chemlon® 217 GIU
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gg67gc_Chemlon-217-GIU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Filler / Reinforcement: Glass Fiber / Fully toughened |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (235°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow 1 | 0.25 to 0.45 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.85 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 86.2 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.5 | % | |
| Break | 5.5 | % | |
| Flexural Modulus | 3790 | MPa | ASTM D790 |
| Flexural Strength | 121 | MPa | ASTM D790 |
| Poisson's Ratio | 0.44 | ASTM C1259 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 140 | J/m | |
| 23°C | 210 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 174 | °C | |
| 1.8 MPa, Unannealed | 157 | °C | |
| Melting Temperature | 216 | °C | ASTM D789 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 2(0.810 mm) | HB | UL 94 | |
| Oxygen Index | 22 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 241 to 257 | °C | |
| Middle Temperature | 252 to 268 | °C | |
| Front Temperature | 257 to 279 | °C | |
| Nozzle Temperature | 257 to 279 | °C | |
| Processing (Melt) Temp | 254 to 277 | °C |
| Note Message | |
|---|---|
| 1 . | Dependent upon molding conditions particularly Mold temperature. |
| 2 . | Chem Polymer measurement according to UL. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PE LT159 (Extrusion/Blow molding) | Sasol Polymers | LDPE | Sasol Polymers PE |
| SLOVAMID® 66 GF 20 GB 10 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| Xuchuan A-8060/B-6018 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| Cellophane™ K220HB20/23 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| LCA® PBT 420 Type | UniPlas, Inc. | PBT | LCA® |