DESLON™ 6 DSC102G9
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DESCO Co., Ltd. |
| Trademark: | DESLON™ 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gg1Iil_DESLON-6-DSC102G9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Descriptions: DESLON™ DSC102G9 is one of the brands which made by Polyamide6 that filled Glass Fiber 45% and reinforced goods. It provides excellent mechanical property, good fluidity property and molding property. Applications: DESLON™ DSC102G9 is one of the most-used for high strength and heat-resisting property goods, such as electronic, electric goods and Automotive parts etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 - 0.30 | % | |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 196 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 12300 | MPa | ASTM D790 |
| Flexural Strength | 304 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 220 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 210 | °C | ASTM D648 |
| Melting Temperature | 220 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 120 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 240 - 250 | °C | |
| Middle Temperature | 250 - 260 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 255 - 270 | °C | |
| Processing (Melt) Temp | 255 - 270 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Injection instructions |
|---|
| Speed: 30 to 60%Pressure 1st: 30 to 70%Pressure 2nd: 30 to 70Holding Pressure: 10 to 30% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIME TPO J-5710 | Prime Polymer Co., Ltd. | PP Random Copolymer | PRIME TPO |
| Titalon® 2300GB | Titan Plastics Compounds Co., Ltd. | Nylon 66 | Titalon® |
| AKROMID® B3 GF 15 9 RM-M black (3512) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| DURANEX® 3400 | Polyplastics Co., Ltd. | PBT | DURANEX® |
| Globalene® SJ3032 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |