Order Products : sales@su-jiao.com
Stanyl® WTP81
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GflrHU_StanylWTP81.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl®WTP81 is a polyamide 46 (nylon 46) material,. This product is available in North America, Europe or Asia Pacific,. Stanyl®The main features of WTP81 are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.18 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 2.0 | -- | % | ISO 294-4 |
| Flow | 2.0 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 3.7 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -- | 3200 | 1000 | MPa | ISO 527-2 |
| 120°C | 800 | -- | MPa | ISO 527-2 |
| 160°C | 650 | -- | MPa | ISO 527-2 |
| 180°C | 600 | -- | MPa | ISO 527-2 |
| 200°C | 500 | -- | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield | 100 | 55.0 | MPa | ISO 527-2 |
| Yield, 120°C | 50.0 | -- | MPa | ISO 527-2 |
| Yield, 160°C | 40.0 | -- | MPa | ISO 527-2 |
| Yield, 180°C | 35.0 | -- | MPa | ISO 527-2 |
| Yield, 200°C | 30.0 | -- | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | ISO 527-2 | |||
| -- | 40 | > 50 | % | ISO 527-2 |
| 120°C | > 50 | -- | % | ISO 527-2 |
| 160°C | > 50 | -- | % | ISO 527-2 |
| 180°C | > 50 | -- | % | ISO 527-2 |
| 200°C | > 50 | -- | % | ISO 527-2 |
| Flexural Modulus | ISO 178 | |||
| -- | 3000 | 900 | MPa | ISO 178 |
| 120°C | 800 | -- | MPa | ISO 178 |
| 160°C | 600 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | 35 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 4.0 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C | 10 | 35 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 280 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 190 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 295 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 8.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
| RTI Elec (0.75 mm) | 150 | -- | °C | UL 746 |
| Thermal Index - 5000 hrs | 152 | -- | °C | IEC 60216 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+9 | ohms·cm | IEC 60093 |
| Dielectric Strength | 25 | 15 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.90 | 22.0 | IEC 60250 | |
| 1 MHz | 3.60 | 1.50 | IEC 60250 | |
| Comparative Tracking Index | 400 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.75 mm | V-2 | -- | IEC 60695-11-10, -20 | |
| 1.5 mm | V-2 | -- | IEC 60695-11-10, -20 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 280 - 320 | °C | |
| Middle Temperature | 300 - 320 | °C | |
| Front Temperature | 300 - 320 | °C | |
| Nozzle Temperature | 300 - 320 | °C | |
| Processing (Melt) Temp | 310 - 320 | °C | |
| Mold Temperature | 80 - 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 - 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Potomer SG5 | Shanghai Potomer International Trade Co., Ltd. | PVC, Rigid | Shanghai Potomer |
| Cytec VTF261 | Cytec Industries Inc. | Adhesive | Cytec |
| Kepital® ET-20 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Optimum® 800 | RAUH Polymers, Inc. | Copolyester | Optimum® |
| Petrotene® PP A3 G18 FR NTLA010 PH325 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |