Quadrant EPP TIVAR® Extrended Wear
| Category: | UHMWPE , Ultra High Molecular Weight Polyethylene |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GfbVnW_Quadrant-EPP-TIVAR-Extrended-Wear.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Quadrant EPP TIVAR® Extrended Wear is an Ultra High Molecular Weight Polyethylene product filled with glass fiber. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | < 0.010 | % | |
| Saturation | < 0.010 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 68 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 703 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 38.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 300 | % | ASTM D638 |
| Flexural Modulus | 752 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 22.8 | MPa | ASTM D790 |
| Compressive Modulus | 648 | MPa | ASTM D695 |
| Compressive Strength (10% Strain, 23°C) | 20.7 | MPa | ASTM D695 |
| Coefficient of Friction (vs. Steel - Static) | 0.12 | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 46.7 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 82 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 1 | 0.0701 | MPa·m/s | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 135 | °C | ASTM D3418 |
| CLTE - Flow 2(-40 to 149°C) | 3.4E-4 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.41 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+10 | ohms | ASTM D257 |
| Dielectric Strength 3 | 91 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.30 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 5.0E-4 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| 3 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-403-M-G50 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| AXELERON™ CC 3485 NT CPD | The Dow Chemical Company | HDPE | AXELERON™ |
| ETILINAS HD4202AA | POLYETHYLENE MALAYSIA SDN BHD | HDPE | ETILINAS |
| GATONE™ 5330FC | Solvay Specialities India Private Limited (SSIPL) | PEEK | GATONE™ |
| LOXIM 830 02C HB | LOXIM Industries Private Limited | PP, Unspecified | LOXIM |