Rynite® 935 NC010
| Category: | PET , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Rynite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GfHGdu_Rynite-935-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% Glass Reinforced Polyethylene Terephthalate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.70 | % | |
| Flow | 0.30 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.83 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.13 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M-Scale | 75 | ||
| R-Scale | 115 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 85.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 9350 | MPa | |
| 1000 hr | 7690 | MPa | |
| Flexural Modulus | 9100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 25 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 235 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B50 |
| Melting Temperature 1 | 252 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.6E-5 | cm/cm/°C | |
| Flow : -40 to 23°C | 2.6E-5 | cm/cm/°C | |
| Transverse | 5.2E-5 | cm/cm/°C | |
| Transverse : -40 to 23°C | 5.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 39 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.50 | ||
| 1 MHz | 4.10 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.030 | ||
| 1 MHz | 0.014 | ||
| Comparative Tracking Index | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| Oxygen Index | 21 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 8511-02 | Colorite Polymers | PVC, Flexible | Unichem |
| CERTENE™ PRM-12C | Muehlstein | PP Random Copolymer | CERTENE™ |
| Hylon® N2000MDHL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| POLYfill PPC T20040 | Polykemi AB | PP Copolymer | POLYfill |
| ESTOPLAST SR 4000GY01 | Ester Industries Ltd. | ABS | ESTOPLAST SR |