LNP™ THERMOCOMP™ D351 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GfAlR9_LNP-THERMOCOMP-D351-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP D351 (experimental grade name as EXTC8143) is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good ductility, Non-Brominated & Non-Chlorinated Flame Retardant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/2.16 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.10 to 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9050 | MPa | ASTM D638 |
| -- | 9080 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 120 | MPa | ASTM D638 |
| Break | 125 | MPa | ISO 527-2/5 |
| Tensile Elongation 3(Break) | 2.4 | % | ASTM D638 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 8400 | MPa | ASTM D790 |
| -- 5 | 7520 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 169 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 179 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 8(23°C) | 39 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 510 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 24.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 116 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 2.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.7E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Nozzle Temperature | 285 to 305 | °C | |
| Processing (Melt) Temp | 285 to 310 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Back Pressure | 0.100 to 0.300 | MPa | |
| Screw Speed | 50 to 90 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 sp=62mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3687 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Royalite R47 | Spartech Plastics | PMMA+PVC | Royalite |
| Diakon® ST15G8 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| Elastron® V V601.A85.N | Elastron USA, Inc. | TPV | Elastron® V |
| Telcar® TL-4001-E | Teknor Apex Company | TPE | Telcar® |