LNP™ STAT-KON™ DX07323 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GeuBxb_LNP-STAT-KON-DX07323-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP STAT-KON DX07323 is a compound based on polycarbonate resin containing conductive fillers. Added features of this compound includes: ESD safe and excellent low-temperature impact performance, intended for compliance to ATEX. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/10.0 kg) | 55 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/10.0 kg) | 50.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.50 | % | Internal Method |
| Flow : 24 hr | 0.40 to 0.70 | % | ASTM D955 |
| Across Flow | 0.50 | % | Internal Method |
| Across Flow : 24 hr | 0.40 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2400 | MPa | ASTM D638 |
| -- | 2400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 45.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/5 |
| Break | 55.0 | MPa | ASTM D638 |
| Break | 44.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | ASTM D638, ISO 527-2/5 | ||
| Yield | 5.0 | % | |
| Break | 9.0 | % | |
| Flexural Modulus | |||
| -- | 2200 | MPa | ASTM D790 |
| -- 2 | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 84.0 | MPa | ASTM D790 |
| -- | 88.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -40°C | 100 | J/m | ASTM D256 |
| 23°C | 180 | J/m | ASTM D256 |
| -40°C 3 | 10 | kJ/m² | ISO 180/1A |
| 23°C 4 | 16 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -40°C | 1500 | J/m | ASTM D4812 |
| 23°C | 1600 | J/m | ASTM D4812 |
| -40°C 5 | 100 | kJ/m² | ISO 180/1U |
| 23°C 6 | 130 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 125 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 7 | 124 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 5.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 5.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 to 1.0E+10 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+6 to 1.0E+10 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (2.50 mm) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 271 to 293 | °C | |
| Middle Temperature | 282 to 304 | °C | |
| Front Temperature | 293 to 316 | °C | |
| Nozzle Temperature | 288 to 310 | °C | |
| Processing (Melt) Temp | 293 to 316 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 GB 25 FR | RTP Company | Nylon 66 | RTP |
| Braskem PE AC 59 | Braskem | HDPE | Braskem PE |
| KumhoSunny PC 2503NH | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |
| Karina WHITE PVC COMP E-854-10/390-B-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plenco 05350 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |