Ultramid® B3M6 BK60564
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GeqWzo_Ultramid-B3M6-BK60564.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3M6 BK60564 is a 30% mineral reinforced, pigmented black injection molding PA6 grade for industrial items requiring high impact strength and very high dimensional stability, excellent laser markability. Applications Typical applications include industrial items. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.90 | -- | % | |
| Water Absorption | ||||
| Saturation | 6.2 | -- | % | ASTM D570 |
| Saturation, 23°C | 6.2 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 2.4 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3700 | -- | MPa | ISO 527-2 |
| Tensile Strength (Break, 23°C) | 85.0 | -- | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 4.9 | -- | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (23°C) | 3270 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.6 | -- | kJ/m² | ISO 179 |
| Notched Izod Impact | ||||
| -40°C | 45 | -- | J/m | ASTM D256 |
| 23°C | 64 | 150 | J/m | ASTM D256 |
| -40°C | 4.0 | -- | kJ/m² | ISO 180 |
| 23°C | 5.5 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 195 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 160 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 120 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | > 1.0E+15 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XANTAR® RX 2125 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| ASTALAC™ ABS M140 | Marplex Australia Pty. Ltd. | ABS | ASTALAC™ |
| DOW™ Electrical & Telecommunications GP K-6050 NT | The Dow Chemical Company | LLDPE | DOW™ Electrical & Telecommunications |
| Sylvin 3290-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ COLORCOMP™ FR23C compound | SABIC Innovative Plastics | ABS | LNP™ COLORCOMP™ |