TAROMID A 280 MB3
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GenkHH_TAROMID-A-280-MB3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAROMID A 280 MB3 is a Polyamide 66 (Nylon 66) product. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 to 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/1.0 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 1.6 to 2.5 | % | |
| Flow | 1.6 to 2.2 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.0 | % | |
| Saturation, 23°C | 7.0 | % | |
| Granule Humidity 1 | < 0.10 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 80.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 65 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2900 | MPa | ISO 178 |
| Flexural Stress 3 | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.8 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 28 | J/m | |
| 23°C | 40 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 90.0 | °C | ISO 75-2/A |
| Continuous Use Temperature | IEC 60216 | ||
| -- 4 | 90.0 | °C | |
| -- 5 | 120 | °C | |
| Vicat Softening Temperature | 240 | °C | ISO 306/B50 |
| Ball Pressure Test (205°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 256 | °C | ISO 11357-3 |
| CLTE - Flow (-30 to 30°C) | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 24 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 3.40 | IEC 60250 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1.0 mm/min |
| 3 . | 1.0 mm/min |
| 4 . | 20000 hrs |
| 5 . | Short Term |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rainmaker Polypropylene ECHPTL40 | Rainmaker Polymers LLC | PP Homopolymer | Rainmaker Polypropylene |
| PURGEX™ 527 | Neutrex, Inc. | Acrylic (PMMA) | Purgex™ |
| Elvax® 3190 | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| Karina BEIGE PVC COMPOUND -E 841-08/184-Y-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1105-8726/GY | Lehmann & Voss & Co. | PEEK | LUVOCOM® |