BJB Polyurethane WC-786 A/B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Geezr6_BJB-Polyurethane-WC-786-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WC-786 A/B produces a high impact, rigid, 80 Shore D material that is commonly used to make clear or tinted castings of all kinds. When used at room temperature castings 1/8" thick or larger can be readily cast. Castings that are less than 1/8" thick generally require pre-warming of materials, molds, and mild post-cure. Easy 1:1 by volume mix ratio for machine casting. Product Highlights:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Part A | 1.077 | g/cm³ | |
| Part B | 1.027 | g/cm³ | |
| Contractility (1.27cm) 1 | 0.50 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Demold Time (25°C) | 6.0 - 8.0 | hr | |
| Work Time (25°C) 2 | 15.0 | min |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Brokfield Viscosity | |||
| Mixed : 25°C | 550 - 650 | mPa·s | |
| Part A : 25°C | 650 | mPa·s | |
| Part B : 25°C | 550 | mPa·s |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Cure Time (25°C) | 5.0 - 7.0 | day |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 78 - 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 27.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 11 - 15 | % | ASTM D638 |
| Flexural Modulus | 1100 | MPa | ASTM D790 |
| Flexural Strength | 49.6 | MPa | ASTM D790 |
| Compressive Modulus | 1900 | MPa | ASTM D695 |
| Compressive Strength | 49.3 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 36 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 62.8 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | ||
| Component B | Mixing ratio by weight: 96, mixing ratio by capacity: 100 | ||
| Shelf Life | 26 | wk |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| In order to achieve maximum physical properties, a post cure with heat is required. BJB recommends 24 hours at ambient temperature, 77°F (25°C), followed by 16 hours at 150-180°F (66-82°C). Support of the part may be required to prevent part deformation during heat cure. |
| Note Message | |
|---|---|
| 1 . | 12"x1/2"x1/2" |
| 2 . | 100g mass - The 15-minute work time is the standard in-stock product. Products with 5, 30, 60, 90,180, and 240-minute work times are availableon a special order basis. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 203-40 | ExxonMobil Chemical | TPV | Santoprene™ |
| Titalon® 3400GF | Titan Plastics Compounds Co., Ltd. | Nylon 12 | Titalon® |
| ANSALAC A09 000 0000 V0 | Daloga srl | ABS | ANSALAC |
| apilon 52c® C 80 | API SpA | TPU-Polyester | apilon 52c® |
| Geon™ Vinyl Flexible A55G0 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |