PREPERM® L380
| Category: | PPE , Polyphenylene Ether |
| Manufacturer: | Premix Oy |
| Trademark: | PREPERM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GebDBP_PREPERM-L380.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PREPERM® L380 is a special compound with elevated dielectric constants of 3.80. PREPERM® L380 is based on Premix proprietary PPE technology. Extremely low dissipation factor (0.0006) makes PREPERM® L380 an excellent material for high frequency applications. PREPERM® L380 offers stable dielectric constant over wide frequency and wide temperature range. PREPERM® retains its physical properties at very low (-78°C) temperatures. PREPERM® L380 can be injection moulded or extruded. Applications include structural parts for antennas in base stations, point to point, wlan, mobile phones etc. Devices made out of PREPERM® L380 can operate at very high frequencies as PREPERM® L380 offers stable performance even at 120 GHz. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, 4.00mm | 53.0 | MPa | ISO 527-2 |
| 4.00 mm | 44.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, 4.00mm | 8.0 | % | ISO 527-2 |
| Fracture, 4.00mm | 25 | % | ISO 527-2 |
| Flexural Modulus (4.00 mm) | 2200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1 | ISO 180 | ||
| -78°C | 12 | kJ/m² | ISO 180 |
| -20°C | 12 | kJ/m² | ISO 180 |
| 23°C | 21 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength 2 | ISO 180 | ||
| -78°C | No Break | ISO 180 | |
| -20°C | No Break | ISO 180 | |
| 23°C | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 178 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 155 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1.00 GHz) | 3.80 | Internal method | |
| Dissipation Factor (1.00 GHz) | 6.0E-4 | Internal method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (4.00 mm) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 290 - 310 | °C | |
| Mold Temperature | 80.0 - 140 | °C | |
| Injection Pressure | 60.0 - 80.0 | MPa | |
| Injection Rate | Moderate |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Melt Temperature | 260 - 280 | °C | |
| Die Temperature | 260 - 300 | °C |
| Extrusion instructions |
|---|
| Tool / roll temperature : 60 - 180°C |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® VA10200 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PCTFE | TEKNIFLEX® |
| TAISOX 8001 | Formosa Plastics Corporation | HDPE | TAISOX |
| Ultramid® 8202 HS | BASF Corporation | Nylon 6 | Ultramid® |
| GAPEX® RPP30EU71HB BLACK | Ferro Corporation | PP, Unspecified | GAPEX® |
| PERLAS® O07F3000B01 | A.D. Compound S.p.A. | PP Homopolymer | PERLAS® |