TABOREX TA 1118 HD
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SILON s.ro |
| Trademark: | TABOREX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gea80S_TABOREX-TA-1118-HD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A chemically-crosslinkable HDPE compound for the production of pipes for domestic hot and cold water, under floor heating and central heating application. It is specially designed to achieve an improved surface quality in co-extrusion or monolayer production processes. TA 1118 HD is a crosslinkable compound made by Silane grafted ethylene polymer. This graft polymer constitutes together with a Masterbatch containing the crosslinking catalyst a "SIOPLAS-SYSTEM". Pipes produced with the SILON grade TA 1118 HD fulfil the requirements of ASTM F876-99a, ASTM F877-99a, CSA 137.5-99, DIN 16892 and all related standards. This system allows the compound to be extruded as a normal thermoplastic polymer, which will attain a high level of crosslinking in the processed form. The final product has all the improved properties associated with crosslinked polyethylene. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.945 | g/cm³ | DIN 53479, ASTM D1505 |
| Apparent Density | 0.56 | g/cm³ | DIN 53466 |
| Melt Mass-Flow Rate (MFR) | Internal method | ||
| 190°C/2.16 kg | 0.90 | g/10 min | Internal method |
| 190°C/5.0 kg | 2.8 | g/10 min | Internal method |
| Moisture Content | % | Internal method | |
| Volatile Matter | % | Internal method | |
| Gel Content 1 | 69 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 21.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 120 | % | ISO 527-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 160 - 170 | °C | |
| Cylinder Zone 2 Temp. | 170 - 180 | °C | |
| Cylinder Zone 3 Temp. | 170 - 190 | °C | |
| Cylinder Zone 4 Temp. | 170 - 190 | °C | |
| Die Temperature | 190 - 220 | °C |
| Extrusion instructions |
|---|
| L/D: >25Compression ratio: 3:1 to 2.5 : 1Head: 200 to 210°CScrew: 70°C to 90 °C |
| Note Message | |
|---|---|
| 1 . | DIN 16892/ ASTM F 876-99a |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® A1 GF 30 LW | A. Schulman Europe | PBT+PET | SCHULADUR® |
| Sindustris PBT GP2157FL | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| CERTENE™ LLBF-121D | Muehlstein | LLDPE | CERTENE™ |
| DJSilicone NE-631 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Purell RP270G | LyondellBasell Industries | PP Random Copolymer | Purell |