Moplen HP565K
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GeRppA_Moplen-HP565K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LyondellBasell Australia's Polypropylene grade HP565K is a medium flow homopolymer with a modified molecular weight distribution and is formulated with an enhanced process stability additive package. HP565K has been developed for the manufacture of high tenacity wearing tapes, ropes and twines. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.5 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 73 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 31.0 | MPa | ISO 527-2 |
| Flexural Modulus | 1400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 3.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 75.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 51.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 155 | °C | ISO 306/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E568 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| TEREZ PA 6 7500 GFN 30 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Unichem 9814 | Colorite Polymers | PVC, Unspecified | Unichem |
| APEX® 85-J023C-10 | Teknor Apex Company | PVC, Flexible | APEX® |
| MAJORIS FG104X | AD majoris | PP, Unspecified | MAJORIS |