Geon™ Vinyl Rigid Extrusion L4067TM
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Rigid Extrusion |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GeG3Tp_Geon-Vinyl-Rigid-Extrusion-L4067TM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Custom molding |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 79 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2230 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 31.6 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 55 | % | ASTM D638 |
| Flexural Modulus 4 | 2340 | MPa | ASTM D790 |
| Flexural Strength 5(Yield) | 79.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm, Compression Molded) | 27 | J/m | ASTM D256 |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 6 | 59.2 | J/cm | ASTM D4226 |
| 23°C 7 | > 178 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, annealed, 3.18mm 8 | 60.7 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm 9 | 49.9 | °C | ASTM D648 |
| CLTE - Flow | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Physical properties based on Geon L4067TM LHB Black 2880. Not capable of meeting UL 94. May meet HB rating. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Type 1, 5.1 mm/min |
| 4 . | 51 mm/min |
| 5 . | 51 mm/min |
| 6 . | Procedure a, .125" |
| 7 . | Procedure B, .125" |
| 8 . | Conditioned at 50 deg.C |
| 9 . | Annealed at 50 deg.C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tectron H2299 | TECTRON Systems Pte Ltd | TPV | Tectron |
| Thermylene® P4-20TC-0521 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| Borstar® FB2310 | Borealis AG | LLDPE | Borstar® |
| Gallonprene® GP200-8 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Karina CLEAR PVC COMPOUND 80/271-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |