Order Products : sales@su-jiao.com
ISOPAK® 569
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Great Eastern Resins Industrial Co Ltd (GRECO) |
| Trademark: | ISOPAK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gdw057_ISOPAK-569.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ISOPAK® 569 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific, Europe, or North America for extrusion or thermoforming. Primary attribute of ISOPAK® 569: Flame Rated. Typical applications include:
|
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 0.50 to 1.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, 3.18 mm) | 44.1 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 30 | % | ASTM D638 |
| Flexural Modulus 1(23°C) | 2260 | MPa | ASTM D790 |
| Flexural Strength 2(Yield, 23°C) | 68.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 290 | J/m | ASTM D256A |
| Notched Izod Impact (Area) 4(23°C) | 33.3 | kJ/m² | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 88.0 | °C | ASTM D648 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| High Amp Arc Ignition (HAI) (1.57 mm) | 200 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (1.57 mm) | 0.00 | mm/min | UL 746 |
| Hot-wire Ignition (HWI) (1.57 mm) | 15 | sec | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.8 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 1/8x1/2x5/2 in |
| 4 . | 1/4" x 1/2" x 5/2" sample |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SNOLEN® EB 0.15/54 | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| Stanyl® TW271F6J10 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| TOTAL Polyethylene D3720 | TOTAL Refining & Chemicals | MDPE | TOTAL Polyethylene |
| KOPLA PET KEG1020 | KOPLA Co., Ltd. | PET | KOPLA PET |
| Sylvin 8739-65FU White 1393 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |