TOTAL Polyethylene Lotrène® Q2018 H
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GdoGBQ_TOTAL-Polyethylene-Lotr-ne-Q2018-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lotrène ® Q2018 H is an ethylene-butene copolymer produced in a gas phase reactor. It is designed for delivering competitive performance in most blown and cast film applications. Lotrène ® Q2018 H can be processed at high output rates with moderate extrusion pressure, good bubble stability and gauge control on blown and cast film machine designed for LLDPE. Lotrène ® Q2018 H can advantageously be blended with LDPE or other PE resins used in blown and cast film mono extrusion or coextrusion to improve film properties. Lotrène ® Q2018 H is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as collation shrink, liners, Form-Fill-Seal, heavy-duty sacks, refuse sacks or other bags and non-packaging applications like agricultural films e.g. tunnel and mulching films. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Modulus | ISO 178 | ||
| 1% secant, MD : 40 µm, blown film | 215 | MPa | ISO 178 |
| 1% secant, TD : 40 µm, blown film | 245 | MPa | ISO 178 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, blown film | 11.0 | MPa | ISO 527-3 |
| TD : Yield, 40 µm, blown film | 11.0 | MPa | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 35.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 33.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 850 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 900 | % | ISO 527-3 |
| Dart Drop Impact 1(40 µm, Blown Film) | 130 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40.0 µm | 55.0 | kN/m | ISO 6383-2 |
| TD : 40.0 µm | 105.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature 2 | 100 | °C | ASTM D1525 |
| Melting Temperature | 121 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 55 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 14 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 210 | °C |
| Extrusion instructions |
|---|
| BUR: 2:1 to 3:1Die gap: > 1.8 mmFigures obtained using laboratory test specimens produced with the following extrusion conditions: 45 mm screw, L/D = 30, die gap = 2.2 mm, BUR = 2.5:1, temperature = 210°C. |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | A120 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melthene® -H 900B (Black) | TOSOH Corporation | EVA | Melthene® -H |
| Staramide PF00AE | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| apigo® D 47T | API SpA | TPO (POE) | apigo® |
| Karina RED COLOR CONCNETRATE 42/155-RG-GE (CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 5196-90FU Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |