Generic Acetal (POM) Homopolymer - Glass Fiber
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GdfO2g_Generic-Acetal-POM-Homopolymer---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Acetal (POM) Homopolymer - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 - 1.63 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.30 - 1.7 | % | ASTM D955 |
| 23°C | 1.2 - 1.7 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.18 - 0.90 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 82 - 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4650 - 11000 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 59.3 - 68.1 | MPa | ASTM D638 |
| Fracture, 23°C | 53.7 - 70.4 | MPa | ASTM D638 |
| 23°C | 66.8 - 78.2 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.6 - 4.2 | % | ASTM D638 |
| Flexural Modulus (23°C) | 3000 - 7600 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 69.6 - 198 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 33 - 72 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 33 - 430 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 159 - 253 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 144 - 165 | °C | ASTM D648 |
| Melting Temperature | 175 - 177 | °C | |
| CLTE - Flow | 4.6E-5 - 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+14 - 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 16 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 121 | °C | |
| Drying Time | 1.9 - 4.0 | hr | |
| Rear Temperature | 182 - 206 | °C | |
| Middle Temperature | 199 - 206 | °C | |
| Front Temperature | 206 - 216 | °C | |
| Processing (Melt) Temp | 200 - 215 | °C | |
| Mold Temperature | 89.3 - 96.7 | °C | |
| Back Pressure | 0.258 - 2.04 | MPa | |
| Screw Speed | 45 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Acetal (POM) Homopolymer - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro PP-HOCC-30GF | Pro Polymers | PP Homopolymer | Pro-Comp™ |
| Shin-Etsu Elastomer KE-551U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| TRANSMARE® 22CT25-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| Geon™ 170 Series 179 | Mexichem Specialty Resins, Inc. | PVC Homopolymer | Geon™ 170 Series |
| HiFill® PC/PBT IM 5720 UV BK | Techmer Engineered Solutions | PC+PBT | HiFill® |