| Injection moulding grade, mineral-reinforced, heat stabilised for technical parts such as engine covers. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.38 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.0 to 6.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % | |
| Viscosity Number (96% H2SO4 (Sulphuric Acid)) | 140 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 205 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6500 | 2300 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 95.0 | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 5.0 | 30 | % | ISO 527-2 |
| Flexural Stress (23°C) | 160 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | |
| 23°C | 5.0 | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | -- | kJ/m² | |
| 23°C | 80 kJ/m² | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 120 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.50 | -- | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.015 | -- | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.50 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Automotive Materials (> 1.00 mm) | + | -- | FMVSS 302 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Melt Temperature | 280 to 300 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAYPRENE® NB221-S4072 | R&P (Pte.) Ltd. | TPE | RAYPRENE® |
| Sinvicomp SGH4000 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Moplen EP548T | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| PERCOM® XG1248 | A. Schulman Europe | PP, Unspecified | PERCOM® |
| Sylvin 9915-72 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |