PRL PPX-FRG20
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GcznCX_PRL-PPX-FRG20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PPX-FRG20 is a Polyphenylene Ether + PS (PPE+PS) product filled with 20% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/11.6 kg) | 1.0 to 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 to 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 106 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 96.5 | MPa | |
| Break, 3.18 mm | 96.5 | MPa | |
| Tensile Elongation (Break, 3.18 mm) | 5.0 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 4960 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.3 | kJ/m² | ISO 179 |
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 80 | J/m | |
| 23°C, 3.18 mm | 91 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 132 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 127 | °C | |
| RTI Elec (1.70 mm) | 65.0 | °C | UL 746 |
| RTI Imp (1.70 mm) | 65.0 | °C | UL 746 |
| RTI Str (1.70 mm) | 65.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.70 mm, ALL) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 249 to 299 | °C | |
| Middle Temperature | 260 to 304 | °C | |
| Front Temperature | 271 to 310 | °C | |
| Processing (Melt) Temp | 288 to 316 | °C | |
| Mold Temperature | 71.1 to 98.9 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M6112 FR | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sinvicomp SFC8201 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| TECHNYL STAR™ SX 218L2 V60 BLACK JA6A | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR™ |
| Hostacom ERC 161N C12380 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Osterlene® LL01020 | Osterman & Company | LLDPE | Osterlene® |