Quadrant EPP CESTILENE HD 1000
| Category: | UHMWPE , Ultra High Molecular Weight Polyethylene |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GbxwNZ_Quadrant-EPP-CESTILENE-HD-1000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Quadrant EPP CESTILENE HD 1000 is an Ultra High Molecular Weight Polyethylene product. It is available in Europe. Applications of Quadrant EPP CESTILENE HD 1000 include bottles, construction applications, electrical/electronic applications, fabrics/fibers and industrial applications. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ISO 1183 |
| Water Absorption (Saturation, 23°C, 1.00 mm) | 0.010 | % | ISO 62 |
| Molecular Weight | 4500000 | g/mol |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Service Temperature - Minimum | -200 | °C |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Relative Weight Loss | Internal Method | ||
| -- 1 | 100 | ||
| -- 2 | 100 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D, 3 sec | 62 | ||
| Shore D, 15 sec | 60 | ||
| Ball Indentation Hardness | 36.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 750 | MPa | ISO 527-2/1B/1 |
| Tensile Stress (Yield) | 19.0 | MPa | ISO 527-2/1B/50 |
| Tensile Strain (Yield) | 15 | % | ISO 527-2/1B/50 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/1B/50 |
| Compressive Stress | ISO 604/1 | ||
| 5% Strain | 14.0 | MPa | |
| 2% Strain | 8.00 | MPa | |
| 1% Strain | 4.50 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -- 3 | > 170 | kJ/m² | Internal Method |
| Partial Break | 110 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 42.0 | °C | ISO 75-2/A |
| Continuous Use Temperature | |||
| -- 4 | 80.0 | °C | |
| -- 5 | 120 | °C | |
| Vicat Softening Temperature | 80.0 | °C | ISO 306/B |
| Melting Temperature | 130 to 135 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 100°C) | 2.0E-4 | cm/cm/°C | |
| Thermal Conductivity (23°C) | 0.40 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm, in Oil) | 45 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 2.10 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 4.0E-4 | ||
| 1 MHz | 1.0E-3 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Oxygen Index | < 20 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Wear test in sand/water slurry |
| 2 . | Wear test on plastics pin on rotating steel disk-tribo system |
| 3 . | Double 15° notch, DIS 11542-2 |
| 4 . | 20000 hrs |
| 5 . | Short periods |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu RTV KE-1871 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| XYRON™ X8610 | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| KYOCERA KE-300TS-1 | KYOCERA Chemical Corporation | Epoxy | KYOCERA |
| INSTRUC PBTGF30 | Infinity LTL Engineered Compounds | PBT | INSTRUC |
| LUVOCOM® 1301-8291 | Lehmann & Voss & Co. | PPS | LUVOCOM® |