Tenac™ LT200
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Tenac™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GbwzXU_Tenac-LT200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tenac™ LT200 is an Acetal (POM) Homopolymer product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™ LT200 include engineering/industrial parts and housings. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.8 to 2.2 | % | Internal Method |
| Water Absorption (23°C, 24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 80 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield | 61.0 | MPa | ISO 527-2 |
| -- | 62.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break | 40 | % | ASTM D638 |
| Break | 35 | % | ISO 527-2 |
| Flexural Modulus | 2600 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 88.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 18.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 172 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 161 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 125 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 92.0 | °C | ISO 75-2/A |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Arc Resistance | 250 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AN0920SB | Ginar Technology Co., LTD. | Nylon 6 | Mapex |
| Vexel PBT B50GF15 | Custom Resins Group | PBT | Vexel |
| TYNEA 4250 | Tyne Plastics LLC. | Acetal (POM) Copolymer | TYNEA |
| Xuchuan XAC-77 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| APEX® 3301-50NT | Teknor Apex Company | PVC, Flexible | APEX® |