VERSIFY™ 2000
| Category: | POP , Plastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | VERSIFY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gbv6zv_VERSIFY-2000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VERSIFY™ 2000 Plastomer is a resin with a low melt flow rate making it suitable for blown film, blow molding, extrusion and thermoforming. It is an excellent sealant and is particularly suitable for use in BOPE structures. It has excellent compatibility with PP and is useful agent to bring softness and temperature performance. Main Characteristics
Applications
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.888 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238, ISO 1133 |
| Total Crystallinity | 35 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, Compression Molded 1 | 96 | ||
| Shore D, Compression Molded 2 | 54 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 26.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 680 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 4(Compression Molded) | 359 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -17.0 | °C | Internal Method |
| Vicat Softening Temperature | 94.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 107 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 20°, 1000 µm, Compression Molded | 108 | ||
| 60°, 1000 µm, Compression Molded | 119 | ||
| Haze (2000 µm, Injection Molded) | 18 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Hardness after 10 seconds. |
| 2 . | Hardness afer 10 seconds. |
| 3 . | 50 mm/min |
| 4 . | Aged two weeks (±3 days) prior to testing. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cheng Yu E2325 | Cheng Yu Plastic Company Limited | PET | Cheng Yu |
| DENKA POVAL PC-5000F | Denka Company Limited | PVOH | DENKA POVAL |
| PENTAMID B GV30 E H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| 3M™ Dyneon™ PTFE Compound APNV063 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Sylvin 9604-80 Clear Black 2104 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |