NEONIT® SK80 L5G
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | SBHPP |
| Trademark: | NEONIT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GbPrqh_NEONITSK80L5G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NEONIT® SK80 L5G is a long glass fiber reinforced epoxy molding compound with excellent long term property retention over a wide temperature range and climate conditions. It is particularly suited for over molding and manufacturing of large commutators. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.77 | g/cm³ | ISO 1183 |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.12 | % | ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.050 | % | ISO 62 |
| Post Shrinkage | -0.030 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 19000 | MPa | ISO 527-2 |
| Tensile Stress | 107 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.70 | % | ISO 527-2 |
| Flexural Modulus | 15000 | MPa | ISO 178 |
| Flexural Stress | 202 | MPa | ISO 178 |
| Compressive Stress | 244 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 43 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 195 | °C | TMA |
| Linear thermal expansion coefficient | TMA | ||
| Flow | 1.1E-5 | cm/cm/°C | TMA |
| Lateral | 4.9E-5 | cm/cm/°C | TMA |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 32 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 GB 15 TFE 15 | RTP Company | Nylon 66 | RTP |
| RTP 1200-75A | RTP Company | TPU, Unspecified | RTP |
| Hylon® N2240MHL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| LUVOCOM® 1105-7794/BL VP | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Plenco 06343 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |