TRYCITE™ 8003
| Category: | PS (HIPS) , Polystyrene Film |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | TRYCITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GbIiNm_TRYCITE-8003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRYCITE™ 8003 Polystyrene Film is a matte finish, translucent, oriented polystyrene film for use in lamination applications. Available thicknesses of 1.0, 1.15, 1.25, 1.5, 2.0, 2.5, and 3.0 mil. |
| General Information | |
|---|---|
| Forms |
|
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 1.0; 1.15; 1.25; 1.5; 2.0; 2.5; 3.0 mil (25; 29; 32; 38; 51; 64; 76 µ) | ||
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD | 2480 | MPa | |
| 1% Secant, TD | 2550 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 55.8 | MPa | |
| TD : Yield | 55.8 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 70 | % | |
| TD : Break | 90 | % | |
| Dart Drop Impact | 200 | g | ASTM D1709 |
| Elmendorf Tear Strength - TD (25 µm) | 7.0 | g | ASTM D1922 |
| Shrink Tension | Internal Method | ||
| MD : 135°C | 1.21 | MPa | |
| TD : 135°C | 0.896 | MPa | |
| Yield | ASTM D4321 | ||
| 25.4 µm | 38.0 | m²/kg | |
| 29.2 µm | 33.0 | m²/kg | |
| 31.8 µm | 30.0 | m²/kg | |
| 38.1 µm | 25.0 | m²/kg | |
| 50.8 µm | 18.9 | m²/kg | |
| 63.5 µm | 15.2 | m²/kg | |
| 76.2 µm | 12.6 | m²/kg |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°) | 20 | ASTM D2457 | |
| Haze | 56 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCLAIR® 2807 | NOVA Chemicals | HDPE | SCLAIR® |
| China PPS MI-hGR50 | Sichuan Deyang Chemical Co., Ltd | PPS | China PPS |
| GPPC ABS D-1000S | GPPC Chemical Co., Ltd. | ABS | GPPC ABS |
| GTPO™ 8202 (Wire & Cable) | S&E Specialty Polymers, LLC | TPO (POE) | GTPO™ |
| Latene® 7-V2 | LATI S.p.A. | PP Homopolymer | Latene® |