Akulon® K224-LGM35
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GbEBy0_Akulon-K224-LGM35.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon® K224-LGM35 is a Polyamide 6 (Nylon 6) material filled with 15% glass fiber and 25% mineral. It is available in Asia Pacific or North America. Important attributes of Akulon® K224-LGM35 are:
Typical application of Akulon® K224-LGM35: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.49 | -- | g/cm³ | ISO 1183 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.7 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | 4800 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | 67.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 6.0 | % | ISO 527-2 |
| Flexural Modulus | 7700 | -- | MPa | ISO 178 |
| Flexural Stress | 165 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | 3.0 | kJ/m² | |
| 23°C | 5.0 | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 25 | -- | kJ/m² | |
| 23°C | 30 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.8E-5 | -- | cm/cm/°C | |
| Transverse | 1.0E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 35 | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.50 | 14.0 | ||
| 1 MHz | 3.30 | 4.50 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 5.0E-3 | 0.32 | ||
| 1 MHz | 0.014 | 0.12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 255 to 265 | °C | |
| Middle Temperature | 265 to 275 | °C | |
| Front Temperature | 265 to 280 | °C | |
| Nozzle Temperature | 260 to 280 | °C | |
| Processing (Melt) Temp | 250 to 285 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® RE 8018 | Teknor Apex Company | PVC, Rigid | APEX® |
| Dion 6694 | Reichhold Chemicals, Inc. | Polyester, TS | Dion |
| Grilamid® 1S XE 4224 nat | EMS-GRIVORY | Nylon 1010 | Grilamid® |
| LUVOCOM® 1800-8608 | LEHVOSS Group | PET | LUVOCOM® |
| Sylvin 8950-65FU Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |