PRL PPX-FR1
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GapFzU_PRL-PPX-FR1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PPX-FR1 is a Polyphenylene Ether + PS (PPE+PS) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/11.6 kg) | 25 to 50 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.18 mm) | 2410 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 55.2 | MPa | |
| Break, 3.18 mm | 48.3 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.18 mm | 3.5 | % | |
| Break, 3.18 mm | 9.0 | % | |
| Flexural Modulus (3.18 mm) | 2280 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 19 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| -30°C, 3.18 mm | 80 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 270 | J/m | ASTM D256 |
| 23°C | 19 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C, 3.18 mm) | 690 | J/m | ASTM D4812 |
| Gardner Impact (3.18 mm) | 16.9 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 87.8 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 82.2 | °C | |
| Vicat Softening Temperature | 103 | °C | ASTM D1525 1 |
| RTI Elec | UL 746 | ||
| 1.50 mm | 110 | °C | |
| 1.70 mm | 110 | °C | |
| 3.00 mm | 110 | °C | |
| RTI Imp | UL 746 | ||
| 1.50 mm | 95.0 | °C | |
| 1.70 mm | 95.0 | °C | |
| 3.00 mm | 95.0 | °C | |
| RTI Str | UL 746 | ||
| 1.50 mm | 110 | °C | |
| 1.70 mm | 110 | °C | |
| 3.00 mm | 110 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.50 mm) | 22 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) (1.50 mm) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 1 | ||
| 1.70 mm | PLC 1 | ||
| 3.00 mm | PLC 1 | ||
| High Voltage Arc Tracking Rate (HVTR) (1.50 mm) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 0 | ||
| 1.70 mm | PLC 0 | ||
| 3.00 mm | PLC 0 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 1.70 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 216 to 266 | °C | |
| Middle Temperature | 227 to 271 | °C | |
| Front Temperature | 238 to 277 | °C | |
| Processing (Melt) Temp | 246 to 274 | °C | |
| Mold Temperature | 54.4 to 76.7 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYCOA Polyamide 2612 | Nycoa (Nylon Corporation of America) | Nylon 612 | NYCOA Polyamide |
| ETILINAS BPD 3220 | POLYETHYLENE MALAYSIA SDN BHD | LLDPE | ETILINAS |
| Karina BLACK PVC COMPOUND 807D48/1-D-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ EC008APQ compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |
| PHOENIX™ 11501 | Phon Tech Industrial Company | SBC | PHOENIX™ |