ENVIROPLAS® ENV17-NC840
| Category: | PEI , Polyether Imide |
| Manufacturer: | ENVIROPLAS®, Inc. |
| Trademark: | ENVIROPLAS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GaStLq_ENVIROPLAS-ENV17-NC840.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Injection Molding Grade, 20% Glass Bead Reinforced, Low Moisture Absorption, Excellent Processability, Excellent mechanical Strength/Stiffness/Dimensional Stability NC840 = To Be Assigned 5 Digit Number Indicating Natural, Black, or Custom Color. The ENV17 Series Products Are Available With Mold Release and/or UV Stabilizer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (24 hr) | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.15 | % | ASTM D570 |
| Balance, 50% RH | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 107 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 4640 | MPa | ASTM D790 |
| Flexural Strength | 175 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 180 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 4.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 4.0E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 316 - 343 | °C | |
| Middle Temperature | 316 - 343 | °C | |
| Front Temperature | 316 - 343 | °C | |
| Nozzle Temperature | 304 - 338 | °C | |
| Mold Temperature | 93.3 - 121 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Injection instructions |
|---|
| Injection Pressure: LowShot Size to barrel Capacity: 50 - 80% |
| Note Message | |
|---|---|
| 1 . | 0.20 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Anjacom® 455-GF10 | Almaak International GmbH | PBT | Anjacom® |
| G-PAEK™ 1120FEP | Gharda Chemicals Ltd. | PEK | G-PAEK™ |
| Sylvin 5224-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| PENTAMID B L10 red 3000/1 | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| VALOX™ V3900WX resin | SABIC Innovative Plastics Asia Pacific | PC+PBT | VALOX™ |