E-RIALFLAME H V2Y 20 SL1
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | E-RIALFLAME |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ga13Vv_E-RIALFLAME-H-V2Y-20-SL1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
V-2 self-extinguishing homopolymer compound with flame-retardant properties, obtained by selected recycling of industrial scraps; low halogens content, free from PBDE and TBBP-A, free from antimony and heavy metals, low fumes emissions. High flowability, remarkable thermal and light stability, specific for applications at sight; in compliance with the requests of the electrotechnical norms for applications in devices for domestic use; available in the versions natural and colored as per sample. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.5 | % | |
| Flow | 1.5 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 75 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 30.0 | MPa | |
| Break, 23°C | 20.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 8.0 | % | |
| Break, 23°C | 250 | % | |
| Flexural Modulus 1(23°C) | 1600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 41.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 55 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 2.0 | kJ/m² | |
| 23°C | 3.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 92.0 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 335 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Glow Wire Flammability Index 2 | IEC 60695-2-12 | ||
| 1.00 mm | 850 | °C | |
| 2.00 mm | 850 | °C | |
| 4.00 mm | 850 | °C | |
| Oxygen Index | 24 | % | ISO 4589-2 |
| Needle Flame Test 3(2.00 mm) | Pass | IEC 60695-2-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 190 to 210 | °C | |
| Mold Temperature | 30.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | Pass |
| 3 . | Method A-B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier HD00763 | Premier Polymers, LLC. | HDPE | Premier |
| RTP 2099 x 121825 E | RTP Company | Nylon, Unspecified | RTP |
| Sindustris PP GP3157F | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Hax™ HFC 0108/4 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| LNP™ LUBRICOMP™ DFL42 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |