ARMAMID® PA HC 30-1AP
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Poly Plastic |
| Trademark: | ARMAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GZtFpP_ARMAMID-PA-HC-30-1AP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ARMAMID® PA HC 30-1AP is a Polyamide 6 (Nylon 6) product. It is available in Europe. |
| General Information |
|---|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density | 1.45 | g/cm³ | |
| Molding Shrinkage | 0.30 to 0.50 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.90 | % | |
| Saturation, 23°C | 6.3 | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | % |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Stress (Yield) | 135 | MPa | |
| Flexural Modulus (23°C) | 13500 | MPa | |
| Flexural Stress | 220 | MPa |
| Impact | Nominal Value | Unit | |
|---|---|---|---|
| Charpy Unnotched Impact Strength | |||
| -40°C | 18 | kJ/m² | |
| 20°C | 32 | kJ/m² |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 192 | °C | |
| Melting Temperature | 220 | °C |
| Electrical | Nominal Value | Unit | |
|---|---|---|---|
| Surface Resistivity 1 | 1.0E+2 | ohms | |
| Volume Resistivity 2 | 1.0E+4 | ohms·cm |
| Flammability | Nominal Value | Unit | |
|---|---|---|---|
| Glow Wire Ignition Temperature | 960 | °C |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Burn Resistant Category | PX-0 |
| Note Message | |
|---|---|
| 1 . | Dry |
| 2 . | Dry |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4590U | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RJM SD101G10 | RJM International, Inc. | PC | RJM |
| SAXALAC™ 120T | SAX Polymers | ABS | SAXALAC™ |
| TYNAB® GM80 | Tyne Plastics LLC. | ABS | TYNAB® |
| Celstran® PP-GF30-0455 P10/16 | Celanese Corporation | PP, Unspecified | Celstran® |