U-polymer PT-3020
| Category: | Polyarylate , Polyarylate |
| Manufacturer: | UNITIKA Plastics Division |
| Trademark: | U-polymer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GZpGBG_U-polymer-PT-3020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| P series resins are resins succeeding the characteristics of the neat polymer, U-100, and improved in flowability and optical properties. Among many super engineering plastics, the resins are few transparent polymer alloys that have heat resistance. The heat-stable P-series resins have variations different in heat resistance in the range from 150 to 175°C. There are few transparent heat-resistant resins among super engineering plastics, and thus P series resins are valuable. The resins have favorable weather resistance, and in particular, the P- 1001 resin is approved by SAE Standard (J576 and J578) and FMVSS Standard (108). Making the most of these characteristics, the resins may be used, for example, as the lenses for automobile lamps. High flow-type resins, P-1001A, and P-3001S, are also available for thin molding products. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.00mm | 0.30 - 0.40 | % | ASTM D955 |
| Transverse flow : 3.00mm | 0.40 - 0.50 | % | ASTM D955 |
| Water Absorption (24 hr, 3.18 mm) | 0.12 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 67.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus | 3800 | MPa | ASTM D790 |
| Flexural Strength | 111 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 165 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow | 3.7E-5 | cm/cm/°C | ASTM D696 |
| Lateral | 4.2E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| CLTE, Flow, ASTM D696: 3.5E-5 to 4.0E-5 cm/cm/°CCLTE, Tranverse, ASTM D696: 3.8E-5 to 4.3E-5 cm/cm/°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VisiJet® M3 ProWax | 3D Systems | Wax | VisiJet® |
| 4MID® 9A32335 I | 4Plas | Nylon 66 | 4MID® |
| 4PET® 9L32320 HL | 4Plas | PET | 4PET® |
| DIAMALOY ABSPC 7801 | Network Polymers, Inc. | PC+ABS | DIAMALOY ABSPC |
| OTECH ALLOY OW128WLG - A/V Jacket | OTECH Corporation | TP, Unspecified | OTECH ALLOY |