Symbios® 3102
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Braskem |
| Trademark: | Symbios® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GZ1twW_Symbios-3102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Braskem Symbios 3102 is a medium melt flow rate terpolymer, designed for use as a heat sealing layer on cast film coextrusion, with heat seal temperature below 110°C on non-treated face. This product does not have slip and anti-blocking agents so it is indicated for customized formularization. This product is appropriate for metalizing and lamination processes. Applications: Sealing layer for cast film coextrusion; Adequate for lamination and metallization processes. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.902 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, Injection Molded) | 83 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 26.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, Injection Molded) | 13 | % | ASTM D638 |
| Flexural Modulus | 800 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 30 µm, Blown Film | 360 | MPa | |
| 1% Secant, TD : 30 µm, Blown Film | 410 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 30 µm, Blown Film | 17.0 | MPa | |
| TD : Yield, 30 µm, Blown Film | 17.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 30 µm, Blown Film | 30 | % | |
| TD : Yield, 30 µm, Blown Film | 13 | % | |
| Seal Initiation Temperature (30 µm, Blown Film) | 101 | °C | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, Injection Molded | 20 | J/m | |
| 23°C, Injection Molded | 45 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, Injection Molded | 79.0 | °C | |
| 1.8 MPa, Unannealed, Injection Molded | 49.0 | °C | |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 1 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm, Blown Film) | 100 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 0.30 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXTEL® 650-BK | MRC Polymers, Inc. | PP Homopolymer | MAXTEL® |
| Telcar® GS7567 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| Unipren® Elastomers B3 PRTA010 75A UP318 | Petropol Industry and Trade of Polymers LTDA | PP+EPDM | Unipren® Elastomers |
| LARIPUR® LPR 9060EF | COIM S.p.A. | TPU-Polyether | LARIPUR® |
| Sylvin 3250-79 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |