Chemlon® 140 MH
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GY2AHL_Chemlon-140-MH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Chemlon® 140 MH is a Polyamide 66 (Nylon 66) material filled with 40% mineral. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Chemlon® 140 MH are:
Typical application of Chemlon® 140 MH: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.70 to 1.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.80 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 89.6 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 1.8 | % | |
| Break | 2.0 | % | |
| Flexural Modulus | 6550 | MPa | ASTM D790 |
| Flexural Strength | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 202 | °C | ASTM D648 |
| Melting Temperature | 257 | °C | |
| CLTE - Flow | 4.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 15 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.810 mm) | HB | UL 94 | |
| Oxygen Index | 27 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 241 to 254 | °C | |
| Middle Temperature | 257 to 274 | °C | |
| Front Temperature | 263 to 282 | °C | |
| Nozzle Temperature | 263 to 279 | °C | |
| Processing (Melt) Temp | 263 to 279 | °C | |
| Mold Temperature | 60.0 to 93.3 | °C | |
| Injection Pressure | 34.5 to 138 | MPa | |
| Screw Speed | 60 to 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC PP M1700 | LG Chem Ltd. | PP Impact Copolymer | SEETEC PP |
| SLOVALEN® PH 56 FRD 1 | Plastcom | PP, Unspecified | SLOVALEN® |
| DOW™ HDPE NG7000 | The Dow Chemical Company | HDPE | DOW™ HDPE |
| Durethan® DP 2802/30 000000 | LANXESS Corporation | Nylon 66 | Durethan® |
| LNP™ VERTON™ RV00CESS compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |