DOW™ HDPE DMDA-8810 NT 7
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GXlZl6_DOW-HDPE-DMDA-8810-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.950 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 128 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 132 | °C | Internal method |
| Extrusion | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Temperature | 302 - 332 | °C | |
| Melt Temperature (Aim) | 316 | °C | |
| Neck-in 1(321°C, 25.4 µm) | 69.9 | mm | Internal method |
| Maximum production line speed 2 | > 7.6 | m/sec | Internal method |
| Minimum coating thickness 3 | 6.4 | µm | Internal method |
| Minimum coating weight 4 | 6.5 | g/m² | Internal method |
| Extrusion instructions |
|---|
| 挤出涂层的制造条件： 螺杆尺寸：3.5 英寸 (89 mm)；30:1 L/D 螺杆类型：单跨 模具间隙：20 密尔 (0.508 mm) 熔体温度：600°F (300°C) 输出：250 磅/小时 螺杆速度：90 rpm |
| Note Message | |
|---|---|
| 1 . | 1.0 Mill (25 µm) coating applied to 50 pounds of kraft paper. |
| 2 . | 1.0 Mill (25 µm) coating applied to 50 pounds of kraft paper. |
| 3 . | 1.0 Mill (25 µm) coating applied to 50 pounds of kraft paper. |
| 4 . | 1.0 Mill (25 µm) coating applied to 50 pounds of kraft paper. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vipel® K022-CCK-18 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| Toraypef® 30040 AS60 | Toray Resin Company | Polyolefin, Unspecified | Toraypef® |
| NuSil MED2-4220 | NuSil Technology | Silicone | NuSil |
| Karina RED COLOR CONCENTRATE 42/ 6-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ADENE® B06CZE-00 | A.D. Compound S.p.A. | PP Homopolymer | ADENE® |