SABIC® HDPE M200056
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GXfU4g_SABIC-HDPE-M200056.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE M200056 is a high density polyethylene copolymer injection moulding grade with a narrow molecular weight distribution. It is typically used for easy mold fill-out and low warpage with a good balance of toughness and stiffness characteristics. Typical applications. SABIC® HDPE M200056 is typically used for injection moulding of food containers, housewares, toys, base cups, caps and closures. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.956 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance 1(60°C, 3.00 mm, Rhodacal-DS10, Compression Molded) | 60.0 | hr | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 62 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1200 | MPa | ISO 527-2/1BA/50 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 2.00 mm, Compression Molded | 28.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 15.0 | MPa | |
| Tensile Elongation 3(Break, 2.00 mm, Compression Molded) | > 200 | % | ASTM D638 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1350 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 28.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C, Compression Molded) | 3.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 85.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 128 | °C | ISO 306/A |
| Melting Temperature (DSC) | 132 | °C | ISO 11357-3 |
| Enthalpy Change | 210 | J/g | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 180 to 250 | °C | |
| Mold Temperature | 15.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2 MPa |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2305 A | RTP Company | PUR, Unspecified | RTP |
| ROPOTEN® T FV-03-223-2 | LUKOIL Bulgaria Ltd. | LDPE | ROPOTEN® T |
| ALCUDIA® EBA PA-1770 | REPSOL | EBA | ALCUDIA® EBA |
| Carbotex KG-10MRA | Kotec Corporation | PC | Carbotex |
| Polimid A 35 GF V0F K | Poliblend S.p.a. | Nylon 66 | Polimid A |