Daplen™ EF267AI
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Daplen™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GXOIuu_Daplen-EF267AI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daplen EF267AI is a 20 % mineral filled polypropylene compound intended for injection moulding. This material has an excellent balance between impact strength and stiffness and is easy to process. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | 1.1 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 61.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2450 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 27.0 | MPa | ISO 527-2/50 |
| Fracture | 10.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield | 4.0 | % | ISO 527-2/50 |
| Fracture | 15 | % | ISO 527-2 |
| Flexural Modulus 2 | 2500 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 3.5% strain | 36.0 | MPa | ISO 178 |
| -- | 38.0 | MPa | ISO 178 |
| Flexural Strain | 5.3 | % | ISO 178 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Atomization- 16 h (100°C) | mg | DIN 75201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | µgC/g | VDA 277 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.8 | kJ/m² | ISO 179/1eA |
| 23°C | 6.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 40 | kJ/m² | ISO 179/1eU |
| 23°C | 120 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C | 2.6 | kJ/m² | ISO 180/1A |
| 23°C | 6.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -20°C | 27 | kJ/m² | ISO 180/1U |
| 23°C | 93 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 56.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 141 | °C | ISO 306/A50 |
| -- | 67.0 | °C | ISO 306/B50 |
| CLTE - Flow 3 | 5.5E-5 | cm/cm/°C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Back Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100-200 m/min |
| Note Message | |
|---|---|
| 1 . | disk |
| 2 . | 2.0 mm/min |
| 3 . | -30°C/80°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXUS ABS ABSLG3030 | Nexus Resin Group, LLC. | ABS | NEXUS ABS |
| Delrin® 327UVE NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Durethan® B 30 S FN30 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Hypro® PP-HP 35NS | Entec Polymers | PP Homopolymer | Hypro® |
| Hostacom EP3307 G82718 | LyondellBasell Industries | PP Copolymer | Hostacom |