INNOPOL® PP CS 2-3516 MO
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GXFlC1_INNOPOL-PP-CS-2-3516-MO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL® CS 2-3516 MO is a 10% talc-filled, elastomer modified compound based on polypropylene block-copolymer. This grade is available in nature and custom coloured form. Recommended application INNOPOL® CS 2-3516 MO is developed for producing injection moulded automotive components. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 820 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 13.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | > 200 | % | ISO 527-2 |
| Flexural Modulus 1 | 800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 35 | kJ/m² | ISO 179/1eA |
| 23°C | 70 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 72.0 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 230 | °C | |
| Middle Temperature | 190 - 230 | °C | |
| Front Temperature | 190 - 230 | °C | |
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold pressure: 30 - 100 % of actual injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LLDPE MG500026 | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| Niche PPHM6BK | Niche Polymer, LLC | PP Homopolymer | Niche |
| 3M™ Dyneon™ Fluoroplastic ET 6235Z | 3M Advanced Materials Division | ETFE | 3M™ Dyneon™ Fluoroplastic |
| Moplen HP640RK | LyondellBasell Industries | PP Homopolymer | Moplen |
| SIBUR Synthetic Rubber NBR 1845 | SIBUR | NBR | SIBUR Synthetic Rubber |